LEXAN™ 123R resin

聚碳酸酯

SABIC Innovative Plastics

产品说明：

Nonhalogenated. 17.5 MFR, for small, intricate parts. UV stabilized. Internal mold release.

LEXAN™ 123R resin 物性表

基本信息

黄卡编号E45587-236866

E207780-100738001

添加剂脱模

紫外线稳定剂

特性无卤

加工方法注射成型

物理性能额定值单位制测试方法比重

ASTM D792--1.20g/cm³ASTM D792--1.19g/cm³ASTM D792特定体积0.835cm³/gASTM D792熔流率（熔体流动速率）(300°C/1.2 kg)18g/10 minASTM D1238收缩率 - 流动(3.20 mm)0.50 到 0.70%内部方法吸水率

ASTM D57024 hr0.15%ASTM D570平衡, 23°C0.35%ASTM D570平衡, 100°C0.58%ASTM D570室外适用性f1

UL 746C硬度额定值单位制测试方法洛氏硬度

ASTM D785M 级70

ASTM D785R 级118

ASTM D785机械性能额定值单位制测试方法抗张强度1

ASTM D638屈服62.1MPaASTM D638断裂65.5MPaASTM D638伸长率2

ASTM D638屈服7.0%ASTM D638断裂110%ASTM D638弯曲模量3(50.0 mm 跨距)2340MPaASTM D790弯曲强度4(屈服, 50.0 mm 跨距)93.1MPaASTM D790泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)10.0mgASTM D1044冲击性能额定值单位制测试方法悬壁梁缺口冲击强度(23°C)690J/mASTM D256无缺口悬臂梁冲击(23°C)3200J/mASTM D4812落锤冲击(23°C)169JASTM D3029拉伸冲击强度5546kJ/m²ASTM D1822热性能额定值单位制测试方法载荷下热变形温度

ASTM D6480.45 MPa, 未退火, 6.40 mm138°CASTM D6481.8 MPa, 未退火, 6.40 mm132°CASTM D648维卡软化温度154°CASTM D15256线形热膨胀系数 - 流动(-40 到 95°C)6.8E-5cm/cm/°CASTM E831比热1260J/kg/°CASTM C351导热系数0.19W/m/KASTM C177RTI Elec130°CUL 746RTI Imp130°CUL 746RTI130°CUL 746